ACRYL 2K MS Resin Topcoat System for Steel Aluminium Plastics UV Resistant

Product Overview

ACRYL 2K is a lacquer system based on MS resins, designed for the creation of topcoats on various substrates such as steel, aluminium or plastics.

The Versatile Profix Topcoat System

ACRYL 2K is a system based on MS resins, designed for the creation of high-quality topcoats on various substrates such as steel, aluminium or plastics. It consists of 23 components, which allows for a wide variety of applications and customisation.

• Gloss coating with standard two-component technology
• Matt coating after the addition of mattifying resin 003
• Longer working time with slowing resin 002, ideal for coating larger surfaces

Technical Specifications

• 23 TONERS
• 7-9 PAINT EFFICIENCY [m2/l]
• 36 MINIMUM SHELF LIFE [months]
• 2:1 MIXING RATIO

Key Benefits

• UV resistant - coating protected against fading and degradation
• High performance - material saving and effective surface coverage
• Based on MS resins - provides durability and quality of coatings
• Easy to apply - quick and convenient coating application
• Versatile application - glossy, matt and larger surface effects possible

Description

Eco binder 2K is a premium additive designed to enhance the gloss of coatings. This innovative product is specially formulated to be used in combination with acrylic mixing system to create an economical and efficient paint mix that delivers outstanding results. The addition of resin does not impair the colour match of the paint, but it's important to keep in mind that the addition of resin may reduce the covering power of the product. Therefore, it's essential to consider this factor when applying the mixture. Additionally, it's crucial to avoid adding any thinners to the paint/resin mixture, as this may negatively affect the quality of the final result.

Specification

• INCREASE IN GLOSS
• EFFICIENT
• SPRAY VISCOSITY: 18-21 sec. DIN Flow Cup 4 mm
• RECOMMENDED SIZES FOR PAINT STRAINER: 125-190 μm
• PAINT EFFICIENCY: 7-9 m2/l
• POT LIFE: 1.5 hrs
• DRY FILM THICKNESS:
  • 1 coat - 25-30 μm
  • 2 coats - 50-60 μm
• MINIMUM SHELF LIFE: 24 months in originally sealed packaging
• VOC: 2004/42/WE/IIB(e)(840) 455

Application

SUBSTRATE PREPARATION:
Once the suitable primer coat has been abraded, clean using silicone remover CP 015 in preparation to apply direct gloss coat.

MIXING RATIO:
2:1
100 parts of Acryl
50 parts of CP 285
10-20% CP 040/ CP 070/ CP 055/ CP 075

SPRAY GUN SETTINGS:
Nozzle size: 1.2-1.4 mm;
Operating pressure: HVLP/RP 1.8-2.0 bar

APPLICATION:
2 full coats allowing flash-off between coats

EVAPORATION TIME AFTER APPLICATION:
5-10 min after coating at 20°C and 65% relative humidity

DRYING:
Drying times at 20°C and 65% relative humidity:
- dust dryness: 15 min
- for assembly: 5 hrs
- thoroughly: 12 hrs

Drying times at 40°C and 65% relative humidity:
- for assembly: 1 hrs

Drying times at 60°C and 65% relative humidity:
- for assembly: 30 min