DINITROL 4010 HIGH TEMPERATURE RUST PROOFING ENGINE COATING WAX 500ML AEROSOL 1125001DINITROL 4010 Corroheat leaves a hard, transparent film that is resistant to both alkali and acids and is heat resistant up to a temperature of 200C. It has a tack free and clean film which facilitates a visual inspection of metal surfaces, reading of labels and numbers etc. BENEFITS Engine protection High temperature resistance High adhesion Longterm protection APPLICATIONS The adhesion and flexibility on rubber and plastic parts at both low and high

DINITROL 4010 Corroheat leaves a hard, transparent film that is resistant to both alkali and acids and is heat resistant up to a temperature of 200°C. It has a tack-free and clean film which facilitates a visual inspection of metal surfaces, reading of labels and numbers etc.
BENEFITS
Engine protection
High temperature resistance
High adhesion
Longterm protection
APPLICATIONS
The adhesion and flexibility on rubber and plastic parts at both low and high temperatures are very good. Appropriate parts to be treated with DINITROL 4010 Corroheat are engine compartments, engines and other parts which have to withstand high temperatures.
METHOD OF USE
DINITROL 4010 Corroheat should be applied on a clean, dry surface. High or low pressure equipment can be used, airless or airmix. Application temperature between 15 – 30°C. Product hardness, flexibility and adhesion increases at higher drying temperatures.
PRE-TREATMENT
Substrates Surfaces shall be dry, clean and free from corrosion.
OVER-COATING
Normally not to be overpainted. For additional information, please consult DINOL GmbH.
STORAGE
The product shouldbe stored at 15 – 30°C and the shelf life is then 2 years in unopened original packages
TECHNICAL DATA
Colour transparent beige
Type of film hard, waxy
Density at 23°C 890 kg/m³
Viscosity at 23°C, DIN 4 25 seconds
Dry matter content 47% by weight
Aromatic part in the solvent 0,5 %
Recommended film thickness wet 120 μm
Recommended film thickness 40 μm
Drying time 120 µm wet, 1 h with optimal ventilation
120 µm wet, 4-6 hours at RT 23°C 50% RH
Low temperature adhesiont -30°C
Effect on car paint none
Removability within 3 months Hydrocarbon solvents
Heat resistance
Short-term 200°C
Long-term 160°C
Salt spray test (drying 24 h, 80°C) 240 hrs 40 microns dry
500 hrs 80 mircrons dry
Available in 10 L Canister / 20 L Pail / 60 L Drum / 208 L Drum